| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據 | 數(shù)據單位 | ||
| 物理性能 | 吸濕率 | 24h | ASTM D570 | 0.03 | % | |
| 玻璃纖維含量 | 30 | % | ||||
| 比重 | ASTM D792 | 1.54 | ||||
| 機械性能 | 硬度 | ASTM D785 | 90 | M | ||
| 引張伸長率 | ASTM D638 | 3.0 | % | |||
| 撓曲模數(shù) | ASTM D790 | 3.0 | kg/cm2 | |||
| 撓曲強度 | ASTM D790 | 1800 | kg/cm2 | |||
| 撓曲強度 | ASTM D790 | 1800 | kg/cm2 | |||
| 撓曲強度 | ASTM D790 | 1800 | kg/cm2 | |||
| 引張強度 | ASTM D638 | 580 | kg/cm2 | |||
| 沖擊強度 | ASTM D256 | 7 | kg.cm/cm | |||
| 撓曲模數(shù) | ASTM D790 | 88000 | kg/cm2 | |||
| 電氣性能 | 體積抵抗率 | ASTM D257 | 1015 | Ω.cm | ||
| CTI | IEC 112 | 175～250V | V | |||
| 誘電正接 | ASTM D150 | 0.01 | 60Hz | |||
| 介電常數(shù) | ASTM D150 | 3.2 | 60Hz | |||
| 耐電弧性 | ASTM D495 | 110 | SEC | |||
| 絕緣破壞強度 | 2mm | ASTM D149 | 19 | KV/mm | ||
| 表面抵抗率 | ASTM D257 | 1013 | Ω | |||
| 熱性能 | 熱膨脹系數(shù) | ASTM D696 | 3 | 10-5cm/cm℃ | ||
| 熱變形溫度 | - | 18.6kg/cm2 | ASTM D648 | 195 | ℃ | |
| - | 4.6kg/cm2 | ASTM D648 | 210 | ℃ | ||
| 熔點 | DSC | 225 | ℃ | |||
| 耐燃性 | 0.8mm | UL94 | V-0 | |||