耐化學PC 耐冰醋酸 四氯化氮浸泡PC塑膠原料
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| UL文件號 |
|
| 外觀 |
|
| 加工方法 |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 比重 | 1.20 | g/cm3 | ASTM D792 |
| Thickness - Layer Capability | 127.0 到 330.2 | μm |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| Volume Resistance 1 | 6.0E+13 到 2.0E+14 | ohms | ASTM D257 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 洛氏硬度 (R 級) | 115 | ASTM D785 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 拉伸模量 2(3.18 mm) | 2280 | MPa | ASTM D638 |
| 抗張強度 3(3.18 mm) | 67.6 | MPa | ASTM D638 |
| 伸長率 4(斷裂, 3.18 mm) | 5.0 | % | ASTM D638 |
| 彎曲模量 5 | 2230 | MPa | ASTM D790 |
| 彎曲強度 6 | 104 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 懸壁梁缺口沖擊強度 (23°C) | 53 | J/m | ASTM D256A |
| 無缺口懸臂梁沖擊 (23°C) | 320 | J/m | ASTM D256 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 載荷下熱變形溫度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 127 | °C | ASTM D648 |
| 玻璃轉化溫度 | 161 | °C | DMA |
| 維卡軟化溫度 | 139 | °C | ASTM D1525 |
| 線形熱膨脹系數(shù) - 流動 | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 介電強度 | 14 到 15 | kV/mm | ASTM D149 |
| 介電常數(shù) 7 | 2.80 到 3.00 | ASTM D150 | |
| 耗散因數(shù) 8 | 5.0E-4 到 6.0E-4 | ASTM D150 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| UL 阻燃等級 | HB | UL 94 |
| 備注 | |
|---|---|
| 1 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 2 . | 類型 1, 5.1 mm/min |
| 3 . | 類型 1, 5.1 mm/min |
| 4 . | 類型 1, 5.1 mm/min |
| 5 . | 方法 I (三點負荷), 1.3 mm/min |
| 6 . | 方法 I (三點負荷), 1.3 mm/min |
| 7 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 8 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
耐化學PC 耐冰醋酸 四氯化氮浸泡PC塑膠原料