SABIC LNP? LUBRICOMP? ECL36 PEI
LNP Lubricomp ECL36 SABIC Innovative Plastics Asia Pacific PEI，聚醚酰亞胺
30% 碳纖維增強(qiáng)材料
SABIC Innovative Plastics
產(chǎn)品說明：
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
LNP*Lubricomp*ECL36是一種基于聚醚酰亞胺樹脂的化合物，含有30%的碳纖維和15%的聚四氟乙烯。這種材料的附加特征是：耐磨。
LNP LUBRICOMP ECL36 is a compound based on Polyetherimide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated.
Also known as: LNP* LUBRICOMP* Compound ECL-4036
Product reorder name: ECL36
填料/增強(qiáng)材料：碳纖維增強(qiáng)材料
添加劑：PTFE潤滑劑
特性：潤滑
RoHS 合規(guī)
加工方法：注射成型
LNP? LUBRICOMP? ECL36 compound 物性表
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
密度 |
1.49 |
g/cm3 |
ISO 1183 |
|
溶化體積流率（MVR）(345°C/10.0 kg) |
4.00 到 6.00 |
cm3/10min |
ISO 1133 |
|
收縮率 |
|
|
ISO 294-4 |
|
垂直流動(dòng)方向 : 24小時(shí) |
1.1 |
% |
ISO 294-4 |
|
流動(dòng)方向 : 24小時(shí) |
0.25 |
% |
ISO 294-4 |
|
吸水率 |
|
|
ISO 62 |
|
23°C, 24 hr |
0.32 |
% |
ISO 62 |
|
平衡, 23°C, 50% RH |
0.21 |
% |
ISO 62 |
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
線形熱膨脹系數(shù) |
|
|
ISO 11359-2 |
|
流動(dòng) : 23 到 60°C |
9.0E-6 |
cm/cm/°C |
ISO 11359-2 |
|
橫向 : 23 到 60°C |
2.8E-5 |
cm/cm/°C |
ISO 11359-2 |
|
比熱 |
1890 |
J/kg/°C |
ASTM E1269 |
|
導(dǎo)熱系數(shù) |
0.33 |
W/m/K |
ASTM D5930 |
|
電氣性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
表面電阻率 |
10 到 1.0E+6 |
ohms |
ASTM D257 |
|
注射 |
額定值 |
單位制 |
|
|
干燥溫度 |
121 到 149 |
°C |
|
|
干燥時(shí)間 |
4.0 到 6.0 |
hr |
|
|
建議的最大水分含量 |
0.020 |
% |
|
|
料筒后部溫度 |
343 到 354 |
°C |
|
|
料筒中部溫度 |
354 到 366 |
°C |
|
|
料筒前部溫度 |
366 到 377 |
°C |
|
|
加工（熔體）溫度 |
360 到 366 |
°C |
|
|
模具溫度 |
121 到 149 |
°C |
|
|
背壓 |
0.344 到 0.689 |
MPa |
|
|
螺桿轉(zhuǎn)速 |
60 到 100 |
rpm |