| 基本性能 | 額定值 | 單位 | 測試方法 |
|---|---|---|---|
| 吸水率 | ASTM D-570 | ||
| (24小時浸漬) | 0.25 | % | |
| (50%相對濕度) | 0.22 | % | |
| (浸漬平衡點) | 0.90 | % |
| 物理性能 | 額定值 | 單位 | 測試方法 |
|---|---|---|---|
| ?？s率 | 1.8-2.0 | % | |
| 比重 | 1.42 | ASTM D-792 |
| 機械性能 | 額定值 | 單位 | 測試方法 |
|---|---|---|---|
| 破裂點拉伸變形量 (100℃) | >260 | % | ASTM D-638 |
| 撓曲系數(shù) (100℃) | 1030 | MPa | ASTM D-790 |
| 拉伸強度 (100℃) | 36 | MPa | ASTM D-638 |
| 彈性系數(shù) (23℃) | 3640 | MPa | ASTM D-638 |
| 拉伸強度 (70℃) | 48 | MPa | ASTM D-638 |
| 壓縮應力 (23℃.10%變形) | 121 | MPa | ASTM D-695 |
| 埃佐沖擊試驗 (缺口-40℃) | 55 | J/m | ASTM D-256 |
| 破裂點拉伸變形量 | ASTM D-638 | ||
| (122℃) | >260 | % | |
| (-55℃) | 10 | % | |
| 撓曲系數(shù) (70℃) | 1720 | MPa | ASTM D-790 |
| 破裂點拉伸變形量 (23℃) | 25 | % | ASTM D-638 |
| 洛氏硬度R | 120 | ASTM D-785 | |
| 撓曲變形強度 (23℃) | 97 | MPa | ASTM D-790 |
| 撓曲系數(shù) (-55℃) | 4730 | MPa | ASTM D-790 |
| 拉伸強度 (23℃) | 69 | MPa | ASTM D-638 |
| 抗剪強度 (23℃) | 66 | MPa | ASTM D-732 |
| 撓曲系數(shù) (23℃) | 3220 | MPa | ASTM D-790 |
| 洛氏硬度M | 94 | ASTM D-785 | |
| 撓曲疲勞忍耐限度 (50%RH.23℃.10周期) | 32 | MPa | ASTM D-671 |
| 撓曲系數(shù) (122℃) | 755 | MPa | ASTM D-790 |
| 破裂點拉伸變形量 (70℃) | 180 | % | ASTM D-638 |
| 拉伸強度 (-55℃) | 101 | MPa | ASTM D-638 |
| 抗拉伸沖擊強度 (23℃) | 250 | kj/m | ASTM D-1822 |
| 壓縮應力 (23℃.1%變形) | 35 | MPa | ASTM D-695 |
| 負載變形量 (140kg/cm,50℃) | 0.5 | % | ASTM D-621 |
| 埃佐沖擊試驗 (無缺口23℃) | 1620 | J/m | ASTM D-256 |
| 拉伸強度 (122℃) | 26 | MPa | ASTM D-638 |
| 埃佐沖擊試驗 (23℃) | 71 | J/m | ASTM D-256 |
| 電氣性能 | 額定值 | 單位 | 測試方法 |
|---|---|---|---|
| 介電常數(shù) (50%RH.23℃.10-10Hz) | 3.7 | Ohm-cm | ASTM D-150 |
| 介電因數(shù) (50%RH.23℃.10Hz) | 0.005 | ASTM D-150 | |
| 介電強度 (2.3mm) | 19.7 | Kv/mm | ASTM D-149 |
| 抗電弧 (3.1mm) | 220 | SEc | ASTM D-495 |
| 容積電阻率 (23℃.0.2%含水量) | 指標|結果-|≥14.9 | Ohm-cm | ASTM D-257 |
| 熱性能 | 額定值 | 單位 | 測試方法 |
|---|---|---|---|
| 線性熱膨脹系數(shù) | ASTM D-696 | ||
| (104-160℃) | 14.9 | 10-5m/m | |
| (60-104℃) | 13.7 | 10-5m/m | |
| 熔點 | 175 | ASTM D-2133 | |
| 熱畸變溫度 (1.8MPa) | 136 | ASTM D-648 | |
| 線性熱膨脹系數(shù) (29-60℃) | 12.2 | 10-5m/m | ASTM D-696 |
| 自燃性 | HB | UL 94 | |
| 熱傳導系數(shù) | 0.37 | W/mk | |
| 線性熱膨脹系數(shù) (-40-29) | 10.4 | 10-5m/m | ASTM D-696 |