PEI 基礎(chǔ)創(chuàng)新塑料（美國(guó)）1000
ULTEM 1000 Resin SABIC Innovative Plastics Asia Pacific PEI，聚醚酰亞胺
SABIC Innovative Plastics
產(chǎn)品說(shuō)明：
Ultem?1000樹(shù)脂是一種無(wú)定形透明聚醚酰亞胺（PEI）塑料，玻璃化轉(zhuǎn)變溫度（Tg）為217°C。這種固有的阻燃樹(shù)脂具有UL94 V0、V2和5VA額定值，符合RoHS。Ultem?1000樹(shù)脂是一種無(wú)鋼筋通用級(jí)樹(shù)脂，具有高耐熱性、高強(qiáng)度和高模量以及耐高溫的廣泛耐化學(xué)性。
ULTEM? 1000 resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM? 1000 resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures.
Tecapei?是一種無(wú)定形熱塑性聚醚酰亞胺（PEI），由SABIC Innovative Plastics的Ultem®1000和2000系列樹(shù)脂制成。無(wú)筋1000系列材料是半透明的琥珀色，結(jié)合了特殊的機(jī)械、熱和電氣性能。2000系列中增加了玻璃纖維增強(qiáng)件，再加上Ensinger專有的擠壓技術(shù)，使Tecapei?具有更高的拉伸強(qiáng)度和剛度，同時(shí)提高了尺寸穩(wěn)定性。優(yōu)異的機(jī)械強(qiáng)度（在室溫下表現(xiàn)出較高的拉伸強(qiáng)度，在高溫下保持很大一部分強(qiáng)度）。玻璃纖維進(jìn)一步提高高溫強(qiáng)度）出色的耐熱性（在高溫下保持其物理特性）對(duì)環(huán)境力的特殊抵抗力（Tecapei?的環(huán)境特性包括其抗應(yīng)力）具有低煙演化的固有阻燃性（根據(jù)UL 94 V-0）高機(jī)械強(qiáng)度、高介電強(qiáng)度和穩(wěn)定性、寬頻率范圍內(nèi)的低耗散系數(shù)、優(yōu)良的機(jī)械加工性和表面處理特性（Tecapei?可使用傳統(tǒng)金屬加工工具輕松加工、涂漆、熱沖壓、印刷或金屬化）天然級(jí)樹(shù)脂為FDA、USP六級(jí)和符合NSF的Tecapei?在醫(yī)療、電子/電氣、微波爐、汽車和飛機(jī)行業(yè)有許多應(yīng)用。
ULTEM? 1000 resin 物性表
特性：高強(qiáng)度，耐化學(xué)性良好，耐熱性，高，通用，無(wú)定形的，阻燃性
用途：通用
外觀：清晰/透明
加工方法：擠出吹塑成型，注射成型
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
比重 |
1.27 |
g/cm3 |
ASTM D792 |
|
熔流率（熔體流動(dòng)速率）(337°C/6.6 kg) |
9.0 |
g/10 min |
ASTM D1238 |
|
收縮率 - 流動(dòng) (3.20 mm) |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
吸水率 |
|
|
ASTM D570 |
|
24 hr |
0.25 |
% |
ASTM D570 |
|
平衡, 23°C |
1.3 |
% |
ASTM D570 |
|
硬度 |
額定值 |
單位制 |
測(cè)試方法 |
|
洛氏硬度 (M 級(jí)) |
109 |
|
ASTM D785 |
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 1 |
3590 |
MPa |
ASTM D638 |
|
抗張強(qiáng)度 2(屈服) |
110 |
MPa |
ASTM D638 |
|
伸長(zhǎng)率 3 |
|
|
ASTM D638 |
|
屈服 |
7.0 |
% |
ASTM D638 |
|
斷裂 |
60 |
% |
ASTM D638 |
|
彎曲模量 4(100 mm 跨距) |
3520 |
MPa |
ASTM D790 |
|
彎曲強(qiáng)度 5(屈服, 100 mm 跨距) |
165 |
MPa |
ASTM D790 |
|
泊松比 |
0.36 |
|
ASTM D638 |
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪) |
10.0 |
mg |
ASTM D1044 |
|
沖擊性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
懸壁梁缺口沖擊強(qiáng)度 (23°C) |
53 |
J/m |
ASTM D256 |
|
無(wú)缺口懸臂梁沖擊 (23°C) |
1300 |
J/m |
ASTM D4812 |
|
反向缺口沖擊 (3.20 mm) |
1300 |
J/m |
ASTM D256 |
|
落錘沖擊 (23°C) |
36.6 |
J |
ASTM D3029 |
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
載荷下熱變形溫度 |
|
|
ASTM D648 |
|
0.45 MPa, 未退火, 6.40 mm |
210 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm |
201 |
°C |
ASTM D648 |
|
維卡軟化溫度 |
219 |
°C |
ASTM D1525 6 |
|
線形熱膨脹系數(shù) |
|
|
ASTM E831 |
|
流動(dòng) : -20 到 150°C |
5.6E-5 |
cm/cm/°C |
ASTM E831 |
|
橫向 : -20 到 150°C |
5.4E-5 |
cm/cm/°C |
ASTM E831 |
|
導(dǎo)熱系數(shù) |
0.22 |
W/m/K |
ASTM C177 |
|
RTI Elec |
170 |
°C |
UL 746 |
|
RTI Imp |
170 |
°C |
UL 746 |
|
RTI |
170 |
°C |
UL 746 |
|
電氣性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
體積電阻率 |
1.0E+17 |
ohms·cm |
ASTM D257 |
|
介電強(qiáng)度 |
|
|
ASTM D149 |
|
1.60 mm, in Air |
33 |
kV/mm |
ASTM D149 |
|
1.60 mm, in Oil |
28 |
kV/mm |
ASTM D149 |
|
3.20 mm, in Oil |
20 |
kV/mm |
ASTM D149 |
|
介電常數(shù) |
|
|
ASTM D150 |
|
100 Hz |
3.15 |
|
ASTM D150 |
|
1 kHz |
3.15 |
|
ASTM D150 |
|
耗散因數(shù) |
|
|
ASTM D150 |
|
100 Hz |
1.5E-3 |
|
ASTM D150 |
|
1 kHz |
1.2E-3 |
|
ASTM D150 |
|
2.45 GHz |
2.5E-3 |
|
ASTM D150 |
|
耐電弧性 7 |
PLC 5 |
|
ASTM D495 |
|
相比耐漏電起痕指數(shù)(CTI) |
PLC 4 |
|
UL 746 |
|
高電弧燃燒指數(shù)(HAI) |
PLC 3 |
|
UL 746 |
|
高電壓電弧起痕速率 (HVTR) |
PLC 2 |
|
UL 746 |
|
熱絲引燃 (HWI) |
PLC 1 |
|
UL 746 |
|
可燃性 |
額定值 |
單位制 |
測(cè)試方法 |
|
UL 阻燃等級(jí) |
|
|
UL 94 |
|
0.400 mm |
V-2 |
|
UL 94 |
|
0.750 mm |
V-0 |
|
UL 94 |
|
3.00 mm |
5VA |
|
UL 94 |
|
極限氧指數(shù) |
47 |
% |
ASTM D2863 |
|
NBS Smoke Density - Flaming, Ds, 4 min |
0.700 |
|
ASTM E662 |
|
注射 |
額定值 |
單位制 |
|
|
干燥溫度 |
149 |
°C |
|
|
干燥時(shí)間 |
4.0 到 6.0 |
hr |
|
|
干燥時(shí)間，最大 |
24 |
hr |
|
|
建議的最大水分含量 |
0.020 |
% |
|
|
建議注射量 |
40 到 60 |
% |
|
|
料筒后部溫度 |
332 到 399 |
°C |
|
|
料筒中部溫度 |
338 到 399 |
°C |
|
|
料筒前部溫度 |
343 到 399 |
°C |
|
|
射嘴溫度 |
343 到 399 |
°C |
|
|
加工（熔體）溫度 |
349 到 399 |
°C |
|
|
模具溫度 |
135 到 163 |
°C |
|
|
背壓 |
0.345 到 0.689 |
MPa |
|
|
螺桿轉(zhuǎn)速 |
40 到 70 |
rpm |
|
|
排氣孔深度 |
0.025 到 0.076 |
mm |
|
|
擠出 |
額定值 |
單位制 |
|
|
干燥溫度 |
138 到 149 |
°C |
|
|
干燥時(shí)間 |
4.0 到 6.0 |
hr |
|
|
建議的最大水分含量 |
0.010 到 0.020 |
% |
|
|
料筒1區(qū)溫度 |
324 到 349 |
°C |
|
|
料筒2區(qū)溫度 |
329 到 357 |
°C |
|
|
料筒3區(qū)溫度 |
329 到 357 |
°C |
|
|
料筒4區(qū)溫度 |
329 到 357 |
°C |
|
|
料筒5區(qū)溫度 |
329 到 357 |
°C |
|
|
接頭溫度 |
329 到 357 |
°C |
|
|
口模溫度 |
327 到 357 |
°C |