Aegis® H135ZP
聚酰胺6
產(chǎn)品說明：
Aegis® H135ZP is a high viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conbs to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermobing properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.
Aegis® H135ZP 物性表
|
基本信息 |
|
|
特性 |
· 均聚物 · 良好的強(qiáng)度 · 良好耐磨損性 · 耐化學(xué)性良好 · 耐熱性，高 · 韌性良好 · 粘度，高 |
|
用途 |
· 包裝 · 流延薄膜 |
|
機(jī)構(gòu)評(píng)級(jí) |
· FDA 21 CFR 177.1500 · 歐洲 2002/72/EC |
|
形式 |
· 粒子 |
|
加工方法 |
· 薄膜擠出 · 吹塑薄膜 · 流延薄膜 · 熱成型 |
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
密度 |
1.13 |
g/cm3 |
ASTM D1505 |
|
熔流率（熔體流動(dòng)速率） (235°C/1.0 kg) |
1.2 |
g/10 min |
ASTM D1238 |
|
吸水率 |
|
|
ASTM D570 |
|
24 hr |
1.6 |
% |
ASTM D570 |
|
飽和 |
9.5 |
% |
ASTM D570 |
|
平衡 |
2.7 |
% |
ASTM D570 |
|
含水量 |
|
% |
ASTM D6869 |
|
相對(duì)粘度 - @ 96% Sulfuric Acid |
3.75 |
|
|
|
粘度 - FAV |
135 |
|
ASTM D789 |
|
薄膜 |
額定值 |
單位制 |
測(cè)試方法 |
|
Elmendorf Tear Strength |
|
|
ASTM D1922 |
|
MD : 23°C |
860 |
N |
ASTM D1922 |
|
TD : 23°C |
990 |
N |
ASTM D1922 |
|
Graves Tear |
|
|
ASTM D1004 |
|
MD : 23°C |
2170 |
N |
ASTM D1004 |
|
TD : 23°C |
2380 |
N |
ASTM D1004 |
|
補(bǔ)充信息 |
額定值 |
單位制 |
|
|
Puncture Index (23°C) 1 |
470.000 |
g/cm3 |
|
|
Puncture Resistance (23°C) 2 |
1100 |
g |
|
|
薄膜 |
額定值 |
單位制 |
測(cè)試方法 |
|
彈性模量 - MD 3 |
660 |
MPa |
ASTM D882 |
|
彈性模量 - TD 4 |
640 |
MPa |
ASTM D882 |
|
抗張強(qiáng)度 5 |
|
|
ASTM D882 |
|
MD : 屈服 |
30.0 |
MPa |
ASTM D882 |
|
TD : 屈服 |
30.0 |
MPa |
ASTM D882 |
|
MD : 斷裂 |
90.0 |
MPa |
ASTM D882 |
|
TD : 斷裂 |
90.0 |
MPa |
ASTM D882 |
|
伸長(zhǎng)率 6 |
|
|
ASTM D882 |
|
MD : 斷裂 |
330 |
% |
ASTM D882 |
|
TD : 斷裂 |
330 |
% |
ASTM D882 |
|
二氧化碳傳輸速率 (23°C) |
72.8 |
cm3/m2/24 hr |
ASTM D1434 |
|
氮傳輸速率 (23°C) |
14.0 |
cm3/m2/24 hr |
ASTM D1434 |
|
氧氣傳輸速率 (23°C) |
40 |
cm3/m2/24 hr |
ASTM D3985 |
|
水氣透過率 (38°C, 100% RH) |
990 |
g/m2/24 hr |
ASTM F1249 |
|
熱性能 |
額定值 |
單位制 |
|
|
熔融溫度 |
220 |
°C |
|
|
補(bǔ)充信息 |
額定值 |
單位制 |
|
|
Extractible Content: 0.7 % |
|
|
|
|
擠出 |
額定值 |
單位制 |
|
|
干燥溫度 |
80.0 |
°C |
|
|
料筒1區(qū)溫度 |
230 到 260 |
°C |
|
|
料筒2區(qū)溫度 |
230 到 260 |
°C |
|
|
料筒3區(qū)溫度 |
230 到 260 |
°C |
|
|
料筒4區(qū)溫度 |
230 到 260 |
°C |
|
|
料筒5區(qū)溫度 |
230 到 260 |
°C |
|
|
接頭溫度 |
260 到 266 |
°C |
|
|
熔體溫度 |
260 到 270 |
°C |
|
|
口模溫度 |
260 |
°C |
|