INCOFLUXR 5 埋弧焊劑
INCOFLUX 5 埋弧焊劑設(shè)計(jì)與MONEL 60焊絲匹配使用，MONEL 60焊絲是一種含銅30％的高鎳合金。這種焊劑的典型應(yīng)用是MONEL 400合金自身之間及其與鐵素體金屬材料之間的開(kāi)坡口焊接。這種焊劑的一個(gè)主要應(yīng)用是與MONEL 60填充金屬相匹配，在碳鋼表面堆焊形成耐蝕保護(hù)層。這種焊劑還可以與Ni-Rod FC 55藥芯焊絲匹配應(yīng)用于鑄鐵之間或鑄鐵與碳鋼之間的焊接，或者是鑄鐵的堆焊。
|
焊接參數(shù)：開(kāi)坡口焊或堆焊：應(yīng)用DCEP電流方式和窄焊道 |
||||||
|
焊絲直徑 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長(zhǎng) |
焊劑層厚度 |
|
|
0.062 in 1.6 mm |
260-280 |
30-33 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
250-300 |
32-35 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
|
電極擺動(dòng)堆焊：應(yīng)用DCEN電流方式，當(dāng)焊絲直徑為0.062 in時(shí)，擺動(dòng)頻率為50-70周／分；當(dāng)焊絲直徑為0.093 in時(shí)，擺動(dòng)頻率為35-60周／分 |
||||||
|
0.062 in 1.6 mm |
260-280 |
32-35 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
300-400 |
34-37 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
儲(chǔ)藏和干燥條件
焊劑密封在未開(kāi)啟的容器中可以無(wú)限期保存。如果焊劑暴露于潮濕環(huán)境中，可以在500oF保溫烘干2小時(shí)或600oF保溫烘干1小時(shí)后使用。
|
焊劑顆粒尺寸
泰勒制網(wǎng)目：10×100目
|
|
包裝 桶蓋上帶有橡膠密封墊圈的60磅聚乙烯桶密封包裝
|
The INCOFLUX 5 submerged arc welding agent is designed to match the MONEL 60 welding wire, which is a high nickel alloy with 30 % copper. The typical application of this kind of flux is MONEL 400 alloy itself and its weld with the open groove of ferritic bl materials. One of the main applications of this flux is to match with the MONEL 60 filler bl, which is surfacing on the surface of carbon steel to b an anticorrosive coating. The flux can also be applied to welding between cast iron or cast iron and carbon steel, or cast iron surfacing, with Ni-Rod FC 55.
Welding beters: open groove welding or surfacing: apply DCEP current and narrow weld path
Electrode dry extension flux layer thickness of wire diameter current/ampere voltage/v welding speed electrode
0.062 in
1.6 mm 260-280 30-33 8-11 in/min
In 200-280 - mm/min 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 250-300 32-35 8-11 in/min
In 200-280 - mm/min 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Electrode swing surfacing welding: the use of DCEN current mode, when the wire diameter is 0.062 in, the oscillation frequency is 50-70 weeks/min; When the wire diameter is 0.093 in, the oscillation frequency is 35-60 weeks/min
0.062 in
1.6 mm 260-280 32-35 4 in/min
100 mm/min in 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 300-400 34-37 4 in/min
100 mm/min in 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Storage and drying conditions
The flux seals can be kept indefiniby in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF.
Flux particle size
Taylor's mesh: 10 times 100
packaging
The barrel cover is covered with a 60 - pound polyethylene barrel sealed with rubber gasket