| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | ASTM D-1238 | 14 | g/10min | |
| 吸水率 | ASTM D-570 | >0.01 | % | ||
| 密度 | ASTM D-792 | 0.90 | g/cm3 | ||
| 機(jī)械性能 | 絕緣強(qiáng)度 | ASTM D-149 | 40 | KV/mm | |
| 斷裂伸張率 | ASTM D-638 | <500 | % | ||
| 洛氏硬度 | ASTM D-785 | 102 | scRale | ||
| 線(xiàn)型成型收縮率 | KPIC Method | 1.0-2.0 | % | ||
| 沖擊強(qiáng)度 | 帶缺口 | ASTM D-256 | 4 | kgf.cm/cm | |
| 撓曲模量 | ASTM D-790 | 17,000 | kgf/cm2 | ||
| 拉伸強(qiáng)度 | ASTM D-638 | 360 | kgf/cm2 | ||
| 電氣性能 | 損耗因素 | ASTM D-150 | 2 | 10-4 | |
| 介電常數(shù) | ASTM D-150 | 2.3 | |||
| 體積電阻率 | ASTM D-257 | 1 | 1017ohm.cm | ||
| 耐電弧性 | ASTM D-495 | 130 | sec. | ||
| 熱性能 | 熔點(diǎn) | ASTM D-3418 | 165 | ℃ | |
| 熱傳導(dǎo) | KPIC Method | 3 | 10-4calcm/cmsec,℃ | ||
| 熱變形溫度 | ASTM D-648 | 110 | ℃ | ||
| 線(xiàn)性膨脹系數(shù) | ASTM D-696 | 11 | 10-5cm/cm℃ | ||
| 比熱容 | KPIC Method | 0.46 | cal/g℃ | ||
| 維卡軟化點(diǎn) | ASTM D-1525 | 153 | ℃ | ||