尺寸公差
標準 |
外徑公差 |
壁厚公差 |
||
GB/T8163-1999 |
D< |
± |
+15/-12.5% |
最?。?/span>+0.45mm |
D≥ |
±1% |
|||
最?。?/span>-0.40mm |
||||
縱向力學性能
標準 |
牌號 |
抗拉強度 |
屈服強度(MPa) ≥ |
延伸率(%) |
|
≤16 |
> |
||||
GB/T8163-1999 |
10 |
335-475 |
205 |
195 |
24 |
20 |
410-550 |
245 |
235 |
20 |
|
Q295 |
430-610 |
295 |
285 |
22 |
|
Q345 |
490-665 |
325 |
315 |
21 |
|
化學成份
標準 |
牌號 |
C |
Si |
Mn |
P≤ |
S≤ |
Ni≤ |
Cu≤ |
Cr≤ |
GB/T8163-1999 |
10 |
0.07-0.14 |
0.17-0.37 |
0.35-0.65 |
0.035 |
0.035 |
0.25 |
0.15 |
0.25 |
20 |
0.17-0.24 |
0.17-0.37 |
0.35-0.65 |
0.035 |
0.035 |
0.25 |
0.25 |
0.25 |
|
Q |
≤0.16 |
≤0.55 |
0.80-1.50 |
0.045 |
0.045 |
0.30 |
0.30 |
0.30 |
|
Q295 B |
≤0.16 |
≤0.55 |
0.80-1.50 |
0.040 |
0.040 |
0.30 |
0.30 |
0.30 |
|
Q |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.045 |
0.045 |
0.30 |
0.30 |
0.30 |
|
Q345 B |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.040 |
0.040 |
0.30 |
0.30 |
0.30 |
|
Q |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.035 |
0.035 |
0.30 |
0.30 |
0.30 |
|
Q345 D |
≤0.18 |
≤0.55 |
1.00-1.60 |
0.030 |
0.030 |
0.30 |
0.30 |
0.30 |
|
Q345 E |
≤0.18 |
≤0.55 |
1.00-1.60 |
0.025 |
0.025 |
0.30 |
0.30 |
0.30 |
高壓鍋爐管是鍋爐管的一種，屬于無縫鋼管類別。制造方法與無縫管相同，但對制造鋼管所用的鋼種有嚴格的要求。高壓鍋爐管使用時經(jīng)常處于高溫和高壓條件，管子在高溫煙氣和水蒸氣的作用下，會發(fā)生氧化和腐蝕。要求鋼管具有高的持久強度，高的抗氧化腐蝕性能，并有良好的組織穩(wěn)定性。高壓鍋爐管主要用來制造高壓和超高壓鍋爐的過熱器管、再熱器管、導氣管、主蒸汽管等。
高壓鍋爐管規(guī)格：8-1240×1-200mm
高壓鍋爐管制造工藝：熱軋、冷拔、熱擴
GB3087-2008 —— 中國國家標準
GB5310 -2008—— 中國國家標準
ASME SA106-------美國鍋爐及壓力容器規(guī)范
ASME SA210 —— 美國鍋爐及壓力容器規(guī)范
ASME SA213 —— 美國鍋爐及壓力容器規(guī)范
DIN17175 —— 聯(lián)邦德國工業(yè)標準
用于低中壓鍋爐（工作壓力一般不大于5.88Mpa，工作溫度在450℃以下）的受熱面管子；用于高壓鍋爐（工作壓力一般在9.8Mpa以上，工作溫度在450℃～650℃之間）的受熱面管子、省煤器、過熱器、再熱器、石化工業(yè)用管等。
規(guī)格及外觀質量：GB5310-95《高壓鍋爐用無縫鋼管》熱軋管的外