阻燃5VA塑料PEI ULTEM 2110R
ULTEM ? Resin 2110R
PEI 基礎(chǔ)創(chuàng)新塑料（美國(guó)）2110R
ULTEM 2110R
10%玻璃纖維填充，增強(qiáng)流動(dòng)Polyetherimide(Tg 217 c)與內(nèi)部脫模。弗吉尼亞州ECO符合，阻燃UL94-V0和5VA。
典型屬性：
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 1160 | kgf/cm2 | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 1180 | kgf/cm2 | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 47100 | kgf/cm2 | ASTM D 638 |
| Flexural Stress, brk, 2.6 mm/min, 100 mm span | 2030 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 53400 | kgf/cm2 | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 40 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.34 | - | ASTM D 792 |
| Melt Flow Rate, 337°C/6.6 kgf | 11.5 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.4 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 1.9 | mm | UL 94 |