熱老化穩(wěn)定PA6 德國(guó)朗盛 BKV15H2.0
PA6 德國(guó)朗盛 BKV15H2.0
Lanxess Durethan BKV 15 H.3 DUS008 000000 Nylon 6, 15% Glass Fiber
產(chǎn)品說(shuō)明：PA 6,15%玻璃纖維,注射成型,熱老化穩(wěn)定。
物理性能：
| Density | 1.228 g/cc | 0.04436 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm | 0.0035 in/in | 150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | 150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577 |
熱性能：
| CTE, linear, Parallel to Flow |
30.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow |
100 μm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 220 °C | 428 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1,-2 |
| Shrinkage | 0.15 % | 0.15 % | post-shrinkage, 150x105x3, 120°C; 4 h; ISO 2577 |
| 0.15 % | 0.15 % | post-shrinkage, transverse, 150x105x3, 120°C; 4 h; ISO 2577 |