專有潤滑劑增強(qiáng)耐磨PA66 美國LNP RF206
PA66 美國液氮 RF206
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66物理性能：
| Density | 1.24 g/cc | 0.0448 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.380 % | 0.380 % | 50% RH, 24 hrs; ASTM D570 |
| 0.660 % | 0.660 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow |
0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
機(jī)械性能：
| Tensile Strength at Break | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.46 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 167 MPa | 24200 psi | ISO 178 |
| 173 MPa | 25100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.06 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.14 J/cm | 2.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.40 | 0.40 | ASTM D3702 Modified |
| K (wear) Factor | 90.6 x 10-8 mm3/N-M | 45.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |