經(jīng)PTFE潤滑碳纖導(dǎo)電尼龍66 美國LNP RCL36
PA66 美國液氮 RCL36
碳纖維增強材料 添加 PTFE潤滑劑 性能特點 導(dǎo)電尼龍 經(jīng)潤滑尼龍LNP LUBRICOMP RCL36 尼龍66樹脂含有聚四氟乙烯的15%，30%的碳纖維化合物。這種材料增加的功能包括：耐磨，導(dǎo)電。
機械性能：
| Tensile Strength at Break | 182 MPa | 26400 psi | ASTM D638 |
| 245 MPa | 35500 psi | ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 22.6 GPa | 3280 ksi | 1 mm/min; ISO 527 |
| 32.4 GPa | 4700 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 372 MPa | 54000 psi | ASTM D790 |
| 396 MPa | 57400 psi | ISO 178 | |
| Flexural Modulus | 18.4 GPa | 2670 ksi | ASTM D790 |
| 22.7 GPa | 3290 ksi | ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.68 J/cm | 20.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m2 | 32.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm3/N-M | 15.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |