物理性能：
| Density | 1.51 g/cc | 0.0546 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0035 cm/cm | 0.0015 - 0.0035 in/in | on Tensile Bar; SABIC Method |
機(jī)械性能：
| Tensile Strength at Break | 219 MPa | 31800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.3 GPa | 1930 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 311 MPa | 45100 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 11.1 GPa | 1610 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m2 | 35.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.75 | 0.75 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D3702 Modified |
| K (wear) Factor | 90.6 x 10-8 mm3/N-M | 45.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
熱性能：
Deflection Temperature at 0.46 MPa (66 psi) 261 °C502 °FFlatw 80*10*4 sp=64mm; ISO 75/BfDeflection Temperature at 1.8 MPa (264 psi) 254 °C489 °FFlatw 80*10*4 sp=64mm; ISO 75/Af